FLAME RETARDANT PC
The common brands of flame retardant PC materials are FRPC-1~FRPC-10. The properties of these 10 brands of flame retardant PC materials are different. They are ultra-thin flame retardant, high flame retardant, high heat-resistant, transparent, anti-aging, anti-aging and anti-low temperature-30 C, anti-aging and anti-low temperature-30 C, 10%, 20% and 10% respectively. Applied to electronic device shell, car lamp shell, dashboard, printer cardboard, printer paper guide rail, electric tool shell, business instrument parts, etc.
| 特性 | 方法 | 测试条件 | 单位 | FRPC-1 | FRPC-2 | FRPC-3 | FRPC-4 | FRPC-5 |
| 超薄阻燃 | 高阻燃 | 高耐热 | 透明 | 抗老化 | ||||
| 密度 | ISO1183 | 23℃ | g/cm³ | 1.2 | 1.2 | 1.2 | 1.2 | 1.2 |
| 熔融指数 | ISO1133 | 300℃/1.2kg | cm³/10min | 20 | 19 | 10 | 10 | 13 |
| 收缩率 | ISO2577 | – | % | 0.5-0.7 | 0.5-0.7 | 0.4-0.6 | 0.4-0.6 | 0.4-0.6 |
| 洛氏硬度 | ISO2039-2 | 1/2″ | R-Scale | 120 | 120 | 122 | 123 | 122 |
| 拉伸强度 | ISO527 | 50mm/min | Mpa | 62 | 60 | 70 | 65 | 65 |
| 延伸率 | ISO527 | 50mm/min | % | 100 | 70 | 120 | 120 | 110 |
| 弯曲强度 | ISO178 | 2mm/min | Mpa | 90 | 90 | 90 | 90 | 85 |
| 弯曲模量 | ISO178 | 2mm/min | Gpa | 2.4 | 2.5 | 2.3 | 2.3 | 2.4 |
| 缺口冲击强度 | ISO180 | Notched,23℃ | KJ/㎡ | 70 | 55 | 70 | 70 | 50 |
| 热变形温度 | ISO75-2 | 18.5kg,120℃/hr
(unannealed) |
℃ | 104 | 88 | 125 | 125 | 115 |
| 软化点温度 | ISO306 | 1kg,50℃/hr
(unannealed) |
℃ | 125 | 110 | 150 | 150 | 148 |
| 燃烧性 | ||||||||
| 燃烧等级 | UL-96 | – | – | 0.6mmV0 | 0.8mmV0 | 1.0mmV0 | 2.5mmV0 | 3mmV0
灼热丝850℃ 1.5mm |
| 加工参数 | ||||||||
| 干燥温度 | – | – | ℃ | 100-105 | 85-90 | 120 | 120 | 110 |
| 干燥时间 | – | – | Hrs | 4-6 | 4-6 | 4-6 | 4-6 | 4-6 |
| 料筒温度 | – | – | ℃ | 260-280 | 250-270 | 280-310 | 280-310 | 260-280 |
| 模具温度 | – | – | ℃ | 70-100 | 70-100 | 70-100 | 70-100 | 70-100 |
| 特性 | 方法 | 测试条件 | 单位 | PC-6600C | PC-618U | EG-8410 | EG-8420 | EG-8430 |
| 抗老化抗低温-30 ℃ | 抗老化抗低-40℃ | 增强10% | 增强20% | 增强30% | ||||
| 密度 | ISO1183 | 23℃ | g/cm³ | 1.2 | 1.2 | 1.27 | 1.35 | 1.44 |
| 熔融指数 | ISO1133 | 300℃/1.2kg | cm³/10min | 11 | 10 | 9 | 8 | 7 |
| 收缩率 | ISO2577 | – | % | 0.4-0.6 | 0.4-0.6 | 0.2-0.4 | 0.1-0.3 | 0.1-0.3 |
| 洛氏硬度 | ISO2039-2 | 1/2’’ | R-Scale | 122 | 122 | 124 | 122 | 122 |
| 拉伸强度 | ISO527 | 50mm/min | Mpa | 60 | 65 | 70 | 90 | 120 |
| 延伸率 | ISO527 | 50mm/min | % | 119 | 120 | 4 | 3 | 2 |
| 弯曲强度 | ISO178 | 2mm/min | Mpa | 90 | 90 | 110 | 120 | 120 |
| 弯曲模量 | ISO178 | 2mm/min | Gpa | 2.3 | 2.3 | 3.4 | 5.3 | 7.6 |
| 缺口冲击强度 | ISO180 | Notched,23℃ | KJ/㎡ | 60 | 60
42（-40 ℃ ） |
8 | 13 | 16 |
| 热变形温度 | ISO75-2 | 18.5kg,120℃/hr
(unannealed) |
℃ | 115 | 125 | 140 | 140 | 140 |
| 软化点温度 | ISO306 | 1kg,50℃/hr
(unannealed) |
℃ | 146 | 150 | 155 | 160 | 165 |
| 燃烧性 | ||||||||
| 燃烧等级 | UL-96 | – | – | 1.5mmV0 | 1.5mmV0 | 1.5mmV0 | 1.5mmV0 | 1.5mmV0
|
| 加工参数 | ||||||||
| 干燥温度 | – | – | ℃ | 110 | 120 | 120 | 120 | 110 |
| 干燥时间 | – | – | Hrs | 4-6 | 4-6 | 4-6 | 4-6 | 4-6 |
| 料筒温度 | – | – | ℃ | 260-280 | 270-290 | 280-310 | 290-320 | 290-320 |
| 模具温度 | – | – | ℃ | 70-100 | 70-100 | 90-120 | 90-120 | 90-120 |